Flow response of a severe plastically deformed two-phase zinc-aluminum alloy

Majid Al-Maharbi, Ibrahim Karaman, Gencaga Purcek

Research output: Contribution to journalArticle

14 Citations (Scopus)

Abstract

A two-phase zinc-aluminum alloy (Zn-8 wt.% Al) has been subjected to severe plastic deformation via equal channel angular extrusion (ECAE). The alloy was successfully extruded at homologous temperatures around 0.5 Tm through various strain paths and magnitudes. Multi-pass ECAE processing following different routes led to the elimination of the as-cast dendritic microstructure and formed a structure of elongated, ribbon-shaped phases. Monotonic tensile tests were conducted at room temperature along the longitudinal axis of the ECAE samples in addition to the directions parallel and perpendicular to the long axis of the elongated hard eutectoid phase particles in order to reveal the effect of microstuctural morphology on the anisotropic flow response. The flow strength levels increased significantly after the first ECAE pass, and then saturated at a slightly higher value after the subsequent passes in route BC. An average increase of about 50% in ultimate tensile strength and about 100 times increase in elongation to failure were achieved after eight ECAE passes following route BC, as compared to the as-cast values. Despite the relative chemical homogenization between the hard and soft phases, the size and distribution of the hard phase in the matrix are found to be the dominant factor controlling the flow response of the present two-phase zinc-aluminum alloy after ECAE. The hard phase size, morphology, and distribution were also found to control the anisotropy in the flow strength and elongation to failure of the ECAE processed samples. Notable flow softening with increasing number of ECAE passes, a general observation for the ECAE processed Zn-Al alloys with Al content more than 12%, was lacking in the present alloy which was attributed to the hardening effect of the fine eutectoid particles in the eutectic matrix overcoming the softening effect of deformation-induced chemical homogenization.

Original languageEnglish
Pages (from-to)518-525
Number of pages8
JournalMaterials Science and Engineering A
Volume527
Issue number3
DOIs
Publication statusPublished - Jan 15 2010

Fingerprint

zinc alloys
Zinc alloys
aluminum alloys
Extrusion
Aluminum alloys
routes
homogenizing
softening
elongation
casts
Elongation
matrices
tensile tests
eutectics
hardening
Eutectics
tensile strength
ribbons
plastic deformation
Hardening

Keywords

  • Equal channel angular extrusion
  • Severe plastic deformation
  • Two-phase alloys
  • Ultrafine-grained (UFG) materials
  • Zn-Al

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanical Engineering
  • Mechanics of Materials

Cite this

Flow response of a severe plastically deformed two-phase zinc-aluminum alloy. / Al-Maharbi, Majid; Karaman, Ibrahim; Purcek, Gencaga.

In: Materials Science and Engineering A, Vol. 527, No. 3, 15.01.2010, p. 518-525.

Research output: Contribution to journalArticle

@article{a20dc28f26464d60918137875df79d2f,
title = "Flow response of a severe plastically deformed two-phase zinc-aluminum alloy",
abstract = "A two-phase zinc-aluminum alloy (Zn-8 wt.{\%} Al) has been subjected to severe plastic deformation via equal channel angular extrusion (ECAE). The alloy was successfully extruded at homologous temperatures around 0.5 Tm through various strain paths and magnitudes. Multi-pass ECAE processing following different routes led to the elimination of the as-cast dendritic microstructure and formed a structure of elongated, ribbon-shaped phases. Monotonic tensile tests were conducted at room temperature along the longitudinal axis of the ECAE samples in addition to the directions parallel and perpendicular to the long axis of the elongated hard eutectoid phase particles in order to reveal the effect of microstuctural morphology on the anisotropic flow response. The flow strength levels increased significantly after the first ECAE pass, and then saturated at a slightly higher value after the subsequent passes in route BC. An average increase of about 50{\%} in ultimate tensile strength and about 100 times increase in elongation to failure were achieved after eight ECAE passes following route BC, as compared to the as-cast values. Despite the relative chemical homogenization between the hard and soft phases, the size and distribution of the hard phase in the matrix are found to be the dominant factor controlling the flow response of the present two-phase zinc-aluminum alloy after ECAE. The hard phase size, morphology, and distribution were also found to control the anisotropy in the flow strength and elongation to failure of the ECAE processed samples. Notable flow softening with increasing number of ECAE passes, a general observation for the ECAE processed Zn-Al alloys with Al content more than 12{\%}, was lacking in the present alloy which was attributed to the hardening effect of the fine eutectoid particles in the eutectic matrix overcoming the softening effect of deformation-induced chemical homogenization.",
keywords = "Equal channel angular extrusion, Severe plastic deformation, Two-phase alloys, Ultrafine-grained (UFG) materials, Zn-Al",
author = "Majid Al-Maharbi and Ibrahim Karaman and Gencaga Purcek",
year = "2010",
month = "1",
day = "15",
doi = "10.1016/j.msea.2009.09.053",
language = "English",
volume = "527",
pages = "518--525",
journal = "Materials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing",
issn = "0921-5093",
publisher = "Elsevier BV",
number = "3",

}

TY - JOUR

T1 - Flow response of a severe plastically deformed two-phase zinc-aluminum alloy

AU - Al-Maharbi, Majid

AU - Karaman, Ibrahim

AU - Purcek, Gencaga

PY - 2010/1/15

Y1 - 2010/1/15

N2 - A two-phase zinc-aluminum alloy (Zn-8 wt.% Al) has been subjected to severe plastic deformation via equal channel angular extrusion (ECAE). The alloy was successfully extruded at homologous temperatures around 0.5 Tm through various strain paths and magnitudes. Multi-pass ECAE processing following different routes led to the elimination of the as-cast dendritic microstructure and formed a structure of elongated, ribbon-shaped phases. Monotonic tensile tests were conducted at room temperature along the longitudinal axis of the ECAE samples in addition to the directions parallel and perpendicular to the long axis of the elongated hard eutectoid phase particles in order to reveal the effect of microstuctural morphology on the anisotropic flow response. The flow strength levels increased significantly after the first ECAE pass, and then saturated at a slightly higher value after the subsequent passes in route BC. An average increase of about 50% in ultimate tensile strength and about 100 times increase in elongation to failure were achieved after eight ECAE passes following route BC, as compared to the as-cast values. Despite the relative chemical homogenization between the hard and soft phases, the size and distribution of the hard phase in the matrix are found to be the dominant factor controlling the flow response of the present two-phase zinc-aluminum alloy after ECAE. The hard phase size, morphology, and distribution were also found to control the anisotropy in the flow strength and elongation to failure of the ECAE processed samples. Notable flow softening with increasing number of ECAE passes, a general observation for the ECAE processed Zn-Al alloys with Al content more than 12%, was lacking in the present alloy which was attributed to the hardening effect of the fine eutectoid particles in the eutectic matrix overcoming the softening effect of deformation-induced chemical homogenization.

AB - A two-phase zinc-aluminum alloy (Zn-8 wt.% Al) has been subjected to severe plastic deformation via equal channel angular extrusion (ECAE). The alloy was successfully extruded at homologous temperatures around 0.5 Tm through various strain paths and magnitudes. Multi-pass ECAE processing following different routes led to the elimination of the as-cast dendritic microstructure and formed a structure of elongated, ribbon-shaped phases. Monotonic tensile tests were conducted at room temperature along the longitudinal axis of the ECAE samples in addition to the directions parallel and perpendicular to the long axis of the elongated hard eutectoid phase particles in order to reveal the effect of microstuctural morphology on the anisotropic flow response. The flow strength levels increased significantly after the first ECAE pass, and then saturated at a slightly higher value after the subsequent passes in route BC. An average increase of about 50% in ultimate tensile strength and about 100 times increase in elongation to failure were achieved after eight ECAE passes following route BC, as compared to the as-cast values. Despite the relative chemical homogenization between the hard and soft phases, the size and distribution of the hard phase in the matrix are found to be the dominant factor controlling the flow response of the present two-phase zinc-aluminum alloy after ECAE. The hard phase size, morphology, and distribution were also found to control the anisotropy in the flow strength and elongation to failure of the ECAE processed samples. Notable flow softening with increasing number of ECAE passes, a general observation for the ECAE processed Zn-Al alloys with Al content more than 12%, was lacking in the present alloy which was attributed to the hardening effect of the fine eutectoid particles in the eutectic matrix overcoming the softening effect of deformation-induced chemical homogenization.

KW - Equal channel angular extrusion

KW - Severe plastic deformation

KW - Two-phase alloys

KW - Ultrafine-grained (UFG) materials

KW - Zn-Al

UR - http://www.scopus.com/inward/record.url?scp=71849099516&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=71849099516&partnerID=8YFLogxK

U2 - 10.1016/j.msea.2009.09.053

DO - 10.1016/j.msea.2009.09.053

M3 - Article

VL - 527

SP - 518

EP - 525

JO - Materials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing

JF - Materials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing

SN - 0921-5093

IS - 3

ER -