Synthesis of 1,4-polybutadiene dendrimer-arborescent polymer hybrids

Mario Gauthier*, Abdul Munam

*المؤلف المقابل لهذا العمل

نتاج البحث: المساهمة في مجلةمراجعة النظراء

26 اقتباسات (Scopus)

ملخص

A divergent synthetic scheme was developed for the preparation of high branching functionality hybrid polymers from carbosilane dendrimer substrates and polybutadiene side chains. Carbosilane dendrimers with 32, 64, or 128 peripheral Si-Cl functional groups were first couple, with 1,2- polybutadienyllithium chains having a number-average molecular weight M n ≈ 1000. The polybutadienc-grafted substrates were then hydrosilylated with dichloromethylsilane and reacted with high 1,4-microstructure content polybutadienyllithium chains to generate high branching functionality dendrimer - arborescent hybrids. Three series of hybrid polymers were synthesized containing 1,4-polybutadiene side chains with M n ≈ 1500, 5000, or 30 000. Size exclusion chromatography analysis of the polymers confirmed that a narrow molecular weight distribution was maintained (Mw/Mn < 1.14). The branching functionality of the arborescent hybrids varied from 140- 335, 160-1110, and 360-2830 for the 32-, 64-, and 128-site coupling precursors, respectively. The experimental branching functionalities attained were lower than the theoretical values due to decreased coupling efficiency within each series, in particular for polymers with longer polybutadiene side chains, apparently due to steric limitations in the grafting reaction.

اللغة الأصليةEnglish
الصفحات (من إلى)3672-3681
عدد الصفحات10
دوريةMacromolecules
مستوى الصوت43
رقم الإصدار8
المعرِّفات الرقمية للأشياء
حالة النشرPublished - أبريل 27 2010
منشور خارجيًانعم

ASJC Scopus subject areas

  • ???subjectarea.asjc.1600.1605???
  • ???subjectarea.asjc.2500.2507???
  • ???subjectarea.asjc.1600.1604???
  • ???subjectarea.asjc.2500.2505???

بصمة

أدرس بدقة موضوعات البحث “Synthesis of 1,4-polybutadiene dendrimer-arborescent polymer hybrids'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا