Polymer light-emitting diodes with spin-polarised charge injection

A. Hayer*, A. Köhler, E. Arisi, I. Bergenti, A. Dediu, C. Taliani, M. Al-Suti, M. S. Khan

*المؤلف المقابل لهذا العمل

نتاج البحث: المساهمة في مجلةConference articleمراجعة النظراء

14 اقتباسات (Scopus)


This study is concerned with the characterisation of the injection properties of the manganite compound La0.7Sr0.3MnO 3 (LSMO) and its use as a spin-polarised anode in polymer light-emitting diodes. Charge carrier injection and electroluminescence in a polymer LED with an LSMO anode is achieved. A dependence of the current-voltage characteristics of LEDs with LSMO anodes on the temperature is observed and compared to the behaviour of LEDs with standard ITO anodes. The temperature dependence is shown to be due to improved hole injection at low temperatures, possibly originating from magnetic ordering upon cooling.

اللغة الأصليةEnglish
الصفحات (من إلى)155-158
عدد الصفحات4
دوريةSynthetic Metals
مستوى الصوت147
رقم الإصدار1-3
المعرِّفات الرقمية للأشياء
حالة النشرPublished - ديسمبر 7 2004
الحدثSupramolecular Approaches to Organic Electronics and Nanotechn. - Strasbourg, France
المدة: مايو ٢٤ ٢٠٠٤مايو ٢٨ ٢٠٠٤

ASJC Scopus subject areas

  • ???subjectarea.asjc.2500.2504???
  • ???subjectarea.asjc.3100.3104???
  • ???subjectarea.asjc.2200.2211???
  • ???subjectarea.asjc.2200.2210???
  • ???subjectarea.asjc.2500.2506???
  • ???subjectarea.asjc.2500.2505???


أدرس بدقة موضوعات البحث “Polymer light-emitting diodes with spin-polarised charge injection'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا