ملخص
X-ray diffraction patterns for Fe0.75Ni0.25-xCrx show that the samples with x = 0 and 0.25 form a single bcc-type phase with a lattice parameter of 2.870 Å, while the samples with x = 0.05 and 0.10 form the bcc-type phase with an additional γ-fcc phase, as a minor phase with a lattice parameter of 3.585 Å. On the other hand all the Fe0.65Ni0.35-xCrx samples show a single γ-fcc phase. The lattice parameter for the Fe0.65Ni0.35-xCrx is found to increase linearly with increasing chromium concentration. Mössbauer spectra for Fe0.75Ni0.25-xCrx show that all the samples are magnetically ordered and some of them have a central paramagnetic line with a very low intensity (between 2 and 15%) for the samples with x = 0, 0.05, and 0.10. However, Mössbauer spectra for Fe0.65Ni0.35-xCrx show that the sample with x = 0 is magnetically ordered and the hyperfine field splitting starts to collapse at x = 0.05 and disappears completely at x = 0.10 and above. The average isomer shift of this system is negative and it decreases with increasing Cr concentration.
اللغة الأصلية | English |
---|---|
الصفحات (من إلى) | 53-59 |
عدد الصفحات | 7 |
دورية | Journal of Alloys and Compounds |
مستوى الصوت | 353 |
رقم الإصدار | 1-2 |
المعرِّفات الرقمية للأشياء | |
حالة النشر | Published - أبريل 7 2003 |
ASJC Scopus subject areas
- ???subjectarea.asjc.2200.2211???
- ???subjectarea.asjc.2200.2210???
- ???subjectarea.asjc.2500.2506???
- ???subjectarea.asjc.2500.2505???