ملخص
In reinforced concrete structures located in hot and humid areas, steel reinforcement is generally vulnerable to deterioration due to corrosion. Corrosion of reinforcement in many cases is considered the main cause of concrete structures deterioration, which in turn requires large budgets for repair and maintenance. This paper presents the experimental results of damaged/repaired reinforced concrete beams. The experimental program consisted of testing reinforced concrete rectangular beam specimen's with/without shear reinforcement and exposed to accelerated corrosion of the longitudinal steel reinforcement on the tension side. Bonding external U-shaped CFRP sheets to restore the strength loss due to corrosion repaired corroded beams without shear reinforcement. The test results showed that corroded beams without stirrups failed in a brittle manner with drop in maximum deflection at failure of approximately 60% compared to the uncorroded beam. Corroded beams with stirrups lost some strength, but failed in ductile manner. Using externally bonded U-shaped CFRP sheets restored the ductility of corroded beams without stirrups and prevented bond failure at the steel concrete interface due to the absence of internal stirrups.
اللغة الأصلية | English |
---|---|
عنوان منشور المضيف | ISEC 2017 - 9th International Structural Engineering and Construction Conference |
العنوان الفرعي لمنشور المضيف | Resilient Structures and Sustainable Construction |
ناشر | ISEC Press |
رقم المعيار الدولي للكتب (الإلكتروني) | 9780996043748 |
حالة النشر | Published - 2017 |
الحدث | 9th International Structural Engineering and Construction Conference: Resilient Structures and Sustainable Construction, ISEC 2017 - Valencia, Spain المدة: يوليو ٢٤ ٢٠١٧ → يوليو ٢٩ ٢٠١٧ |
Other
Other | 9th International Structural Engineering and Construction Conference: Resilient Structures and Sustainable Construction, ISEC 2017 |
---|---|
الدولة/الإقليم | Spain |
المدينة | Valencia |
المدة | ٧/٢٤/١٧ → ٧/٢٩/١٧ |
ASJC Scopus subject areas
- ???subjectarea.asjc.2200.2205???
- ???subjectarea.asjc.2200.2215???