Study of date palm stem as raw material in preparation of activated carbon

O. Houache, R. Al-Maamari, B. Al-Rashidi, B. Jibril

Research output: Contribution to journalArticle

3 Citations (Scopus)

Abstract

Activated carbon adsorbent was prepared using Omani date palm tree stem as a precursor. Precursor samples were subjected to thermal treatment (at 400, 500 and 600 °C) before or after impregnation with either H3PO4 (85 wt %) or KOH (3 wt %). The activated carbon obtained was characterized by BET (surface area and porosity), Gas Pycnometry (true density) and SEM (texture). Sample subjected to carbonization, without chemical activation, exhibited low surface areas ~ 1.0 m2/g at 400 and 500 °C and 124 m2/g at 600 °C. Further treatment of such samples with either the acid or the base did not show improvement in surface area or other properties. Impregnations of the precursor with acid before carbonization significantly improved the surface area to as high as 1,100 m2/g at a carbonization temperature of 500 °C. Thus, activated carbon with a moderate surface area could be produced from date palm stem using low carbonization temperature.

Original languageEnglish
Pages (from-to)47-51
Number of pages5
JournalJournal of Engineering Research
Volume6
Issue number2
Publication statusPublished - 2009

Fingerprint

Activated carbon
Carbonization
Raw materials
Impregnation
Acids
Density (specific gravity)
Adsorbents
Textures
Porosity
Chemical activation
Heat treatment
Temperature
Scanning electron microscopy
Gases

Keywords

  • Activated carbon
  • BET surface area
  • Chemical activation
  • Date palm stem
  • Porosity
  • SEM

ASJC Scopus subject areas

  • Engineering(all)

Cite this

Study of date palm stem as raw material in preparation of activated carbon. / Houache, O.; Al-Maamari, R.; Al-Rashidi, B.; Jibril, B.

In: Journal of Engineering Research, Vol. 6, No. 2, 2009, p. 47-51.

Research output: Contribution to journalArticle

@article{abfaf79973504c7cb630df38d7e8d44f,
title = "Study of date palm stem as raw material in preparation of activated carbon",
abstract = "Activated carbon adsorbent was prepared using Omani date palm tree stem as a precursor. Precursor samples were subjected to thermal treatment (at 400, 500 and 600 °C) before or after impregnation with either H3PO4 (85 wt {\%}) or KOH (3 wt {\%}). The activated carbon obtained was characterized by BET (surface area and porosity), Gas Pycnometry (true density) and SEM (texture). Sample subjected to carbonization, without chemical activation, exhibited low surface areas ~ 1.0 m2/g at 400 and 500 °C and 124 m2/g at 600 °C. Further treatment of such samples with either the acid or the base did not show improvement in surface area or other properties. Impregnations of the precursor with acid before carbonization significantly improved the surface area to as high as 1,100 m2/g at a carbonization temperature of 500 °C. Thus, activated carbon with a moderate surface area could be produced from date palm stem using low carbonization temperature.",
keywords = "Activated carbon, BET surface area, Chemical activation, Date palm stem, Porosity, SEM",
author = "O. Houache and R. Al-Maamari and B. Al-Rashidi and B. Jibril",
year = "2009",
language = "English",
volume = "6",
pages = "47--51",
journal = "Journal of Engineering Research",
issn = "1726-6009",
publisher = "Sultan Qaboos University",
number = "2",

}

TY - JOUR

T1 - Study of date palm stem as raw material in preparation of activated carbon

AU - Houache, O.

AU - Al-Maamari, R.

AU - Al-Rashidi, B.

AU - Jibril, B.

PY - 2009

Y1 - 2009

N2 - Activated carbon adsorbent was prepared using Omani date palm tree stem as a precursor. Precursor samples were subjected to thermal treatment (at 400, 500 and 600 °C) before or after impregnation with either H3PO4 (85 wt %) or KOH (3 wt %). The activated carbon obtained was characterized by BET (surface area and porosity), Gas Pycnometry (true density) and SEM (texture). Sample subjected to carbonization, without chemical activation, exhibited low surface areas ~ 1.0 m2/g at 400 and 500 °C and 124 m2/g at 600 °C. Further treatment of such samples with either the acid or the base did not show improvement in surface area or other properties. Impregnations of the precursor with acid before carbonization significantly improved the surface area to as high as 1,100 m2/g at a carbonization temperature of 500 °C. Thus, activated carbon with a moderate surface area could be produced from date palm stem using low carbonization temperature.

AB - Activated carbon adsorbent was prepared using Omani date palm tree stem as a precursor. Precursor samples were subjected to thermal treatment (at 400, 500 and 600 °C) before or after impregnation with either H3PO4 (85 wt %) or KOH (3 wt %). The activated carbon obtained was characterized by BET (surface area and porosity), Gas Pycnometry (true density) and SEM (texture). Sample subjected to carbonization, without chemical activation, exhibited low surface areas ~ 1.0 m2/g at 400 and 500 °C and 124 m2/g at 600 °C. Further treatment of such samples with either the acid or the base did not show improvement in surface area or other properties. Impregnations of the precursor with acid before carbonization significantly improved the surface area to as high as 1,100 m2/g at a carbonization temperature of 500 °C. Thus, activated carbon with a moderate surface area could be produced from date palm stem using low carbonization temperature.

KW - Activated carbon

KW - BET surface area

KW - Chemical activation

KW - Date palm stem

KW - Porosity

KW - SEM

UR - http://www.scopus.com/inward/record.url?scp=77957775897&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=77957775897&partnerID=8YFLogxK

M3 - Article

VL - 6

SP - 47

EP - 51

JO - Journal of Engineering Research

JF - Journal of Engineering Research

SN - 1726-6009

IS - 2

ER -