The influence of ball milling and subsequent calcination on the formation of LiFeO2

H. M. Widatallah, C. Johnson, F. J. Berry*

*المؤلف المقابل لهذا العمل

نتاج البحث: المساهمة في مجلةمراجعة النظراء

23 اقتباسات (Scopus)

ملخص

The influence of ball milling and subsequent calcination of a 1:1 molar mixture of α-Fe2O3 and Li2CO3 on the formation of LiFeO2 has been investigated. Pre-milling was found to lower the temperature of ferrite formation by ca. 200°C and a thermally stable γ-LiFeO2 phase was found to form in the temperature range 500-600°C. Slow cooling of the pre-milled mixture calcined at higher temperatures resulted in the formation of some LiFe5O8.

اللغة الأصليةEnglish
الصفحات (من إلى)4621-4625
عدد الصفحات5
دوريةJournal of Materials Science
مستوى الصوت37
رقم الإصدار21
المعرِّفات الرقمية للأشياء
حالة النشرPublished - نوفمبر 1 2002
منشور خارجيًانعم

ASJC Scopus subject areas

  • ???subjectarea.asjc.2500???
  • ???subjectarea.asjc.2200.2211???
  • ???subjectarea.asjc.2200.2210???

بصمة

أدرس بدقة موضوعات البحث “The influence of ball milling and subsequent calcination on the formation of LiFeO2'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا