Study the effect of ultrasonic irradiation and surfactant/fe ions weight ratio on morphology and particle size of magnetite nanoparticles synthesised by co-precipitation for medical application

S. Saloomeh Azimipour Meibod, Peyman Pourafshary, Hamid Reza Madaah Hosseini

نتاج البحث: المساهمة في مجلةمراجعة النظراء

1 اقتباس (Scopus)

ملخص

A biocompatible ferrofluid have been prepared by coprecipitation of FeCl 2.4H 2O and FeCl 3.6H 2O under ultrasonic irradiation and with NaOH as alkaline agent. Cystein was also used as capping agent in the solution. Magnetic properties of the produced ferrofluid were then determined by VSM test and magnetite nanoparticles were characterized by XRD and TEM techniques. The effect of surfactant to Fe ion weight ratio was also studied during this project by using two different amount of Dextran. Results showed the presence of a biocompatible superparamagnetic ferrofluid including magnetite nanoparticles with particle size ranging under 20 nm. The increase in the surfactant content results in the narrowing of the size distribution and reduction of the particle size and more solution stability.

اللغة الأصليةEnglish
الصفحات (من إلى)457-460
عدد الصفحات4
دوريةWorld Academy of Science, Engineering and Technology
مستوى الصوت64
حالة النشرPublished - 2010
منشور خارجيًانعم

ASJC Scopus subject areas

  • ???subjectarea.asjc.2200???

بصمة

أدرس بدقة موضوعات البحث “Study the effect of ultrasonic irradiation and surfactant/fe ions weight ratio on morphology and particle size of magnetite nanoparticles synthesised by co-precipitation for medical application'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا