Radiation-hardness studies of high OH- content quartz fibres irradiated with 500 MeV electrons

I. Dumanoglu, N. Akchurin, U. Akgun, S. Ayan, P. Bruecken, E. Eskut, A. Fenyvesi, A. Kayis Topkasu, N. Koca, K. Makonyi, J. P. Merlo*, D. Novak, Y. Onel, G. Onengut, A. Polatoz, I. Schmidt, M. Serin, M. Zeyrek

*المؤلف المقابل لهذا العمل

نتاج البحث: المساهمة في مجلةمراجعة النظراء

37 اقتباسات (Scopus)

ملخص

We investigated the darkening of nine high OH- fibre types irradiated with 500 MeV electrons from the Linac Injector of LEP (LIL) at CERN. The transmission of Xe light was measured in situ in the 350-800 nm range. The induced attenuation at 450 nm is typically 1.52 ± 0.15 dB/m for a 100 Mrad absorbed dose. Two-parameter fits for darkening and recovery are presented. After irradiation the tensile strength remains essentially unchanged. For Polymicro quartz core fibres the tensile strength is typically 4.6 ± 0.4 GPa.

اللغة الأصليةEnglish
الصفحات (من إلى)444-455
عدد الصفحات12
دوريةNuclear Instruments and Methods in Physics Research, Section A: Accelerators, Spectrometers, Detectors and Associated Equipment
مستوى الصوت490
رقم الإصدار3
المعرِّفات الرقمية للأشياء
حالة النشرPublished - سبتمبر 11 2002
منشور خارجيًانعم

ASJC Scopus subject areas

  • ???subjectarea.asjc.3100.3106???
  • ???subjectarea.asjc.3100.3105???

بصمة

أدرس بدقة موضوعات البحث “Radiation-hardness studies of high OH- content quartz fibres irradiated with 500 MeV electrons'. فهما يشكلان معًا بصمة فريدة.

قم بذكر هذا