Transparent co-doped TiO2 thin films have been fabricated by sol-gel dip-coating. The doping is achieved using low concentrations of neodymium (Nd), silver (Ag), and copper (Cu). A significant effect of doping is noticed on the morphology and optical properties of thin films. XRD analysis confirms the formation of a pure anatase phase with a deterioration of the crystallinity upon doping. The co-doped TiO2 thin films present larger crystallite size compared to other films. The surface roughness revealed by AFM increases from 0.9 nm for pure TiO2 up to 5 nm for doped thin films. UV-vis spectroscopy shows that the bandgap energy slightly decreased for co-doped Ag-Nd/TiO2 and Cu-Nd/TiO2. Photocatalytic degradation of MB significantly decreases upon doping. A mechanism based on combined effects of doping, annealing and nature of substrate is proposed to explain the photodegradation behaviour.
اللغة الأصلية | English |
---|---|
الصفحات (من إلى) | 784-794 |
عدد الصفحات | 11 |
دورية | Surface Engineering |
مستوى الصوت | 37 |
رقم الإصدار | 6 |
المعرِّفات الرقمية للأشياء | |
حالة النشر | Published - 2021 |
منشور خارجيًا | نعم |
ASJC Scopus subject areas
- ???subjectarea.asjc.3100.3104???
- ???subjectarea.asjc.3100.3110???
- ???subjectarea.asjc.2500.2508???
- ???subjectarea.asjc.2500.2505???