ZnO varistor materials were prepared by a sol gel route with subsequent drying and calcination. Varistor discs fabricated from these materials were subjected to a two step sintering schedule. Therefore in a typical experiment, the samples were heated to 1000°C, then allowed to cool for over 30 min to 900°C and held there for 6 h. The results were compared with commercial varistor samples sintered in a similar way. Considerably higher breakdown voltages were obtained for the varistors made from nanosample (1192±30 V mm-1) compared with the commercial samples (723 ±30 V mm-1) sintered under the same experimental conditions. The sintered materials were characterised by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and density measurements.
اللغة الأصلية | English |
---|---|
الصفحات (من إلى) | 158-160 |
عدد الصفحات | 3 |
دورية | Advances in Applied Ceramics |
مستوى الصوت | 105 |
رقم الإصدار | 3 |
المعرِّفات الرقمية للأشياء | |
حالة النشر | Published - يونيو 2006 |
منشور خارجيًا | نعم |
ASJC Scopus subject areas
- ???subjectarea.asjc.2500.2503???
- ???subjectarea.asjc.2200.2209???